THS Heat shrinkable tube for terminals and crimp splices

Product > Heat Shrinkable for Terminals and Crimp Splices > THS Heat shrinkable tube for terminals and crimp splices

THS Heat shrinkable tube for terminals and crimp splices

Applications

THS is a heat-shrinkable tube made of polyolefin, and the inner layer is coated with a polyamide hot melt adhesive. Suitable for terminals and crimp joints, providing excellent water and corrosion resistance, fully insulated and protected from electrical connections.

Characteristics

Shrinkage ratio 3：1

Abrasion and corrosion resistance

Water proof and moisture resistance

Operating temperature range

Operating temperature : -55℃～125℃

Minimum shrink temperature : 80?C

fully recovery temperature : 130?C

Technical Indicators

Test Item

Characteristics

Test condition

Unaged

Tensile strength

Min. 18MPa

Room temp.

Elongation

Min. 200%

Aged

Tensile strength

Min. 11.5MPa

158℃/7 days

Elongation

Min. 100%

Voltage withstand and breakdown Voltage(Unaged)

Withstand 2.5 KV for 1minute and breakdown

Room temp.

Voltage withstand and breakdown Voltage(Aged)

Withstand 2.5 KV for 1minute and breakdown at least half of unaged breakdown voltage

158℃/7 days

Copper corrosion

No corrosion of bare copper

158℃/7 days

Copper stability

No sign of degradation Min.Elongation 100%

158℃/7 days

Cold bend

No crack

-30℃/4 hrs

Maximum secant modulus(2%)

250 MPa

-

Volume resistivity

Min.1014Ω-cm

-

Heat shock

No crack

250℃/4 hrs

Product Dimensions

Part No.

As supplied（mm）

After recovered（mm）

ID

WT

ID(MAX)

WT

THS-Φ4.8

Φ4.8±0.3

0.50±0.1

Φ1.4

1.1±0.1

THS-Φ5.8

Φ5.8±0.3

0.60±0.1

Φ1.7

1.2±0.1

THS-Φ6.8

Φ6.8±0.3

0.65±0.1

Φ2.1

1.4±0.1

THS-Φ7.0

Φ7.0±0.3

0.65±0.1

Φ2.5

1.5±0.1

THS-Φ8.3

Φ8.3±0.3

0.70±0.1

Φ3.0

1.65±0.1